- The simple Way to create outstanding water-based Nail Polishes
Product Range Product INCI Characteristics 100 200 Base Coat Top Coat Natural Remover Aqua, Polyacrylate-42, Dibutyl Sebacate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Aqua, Polyacrylate-42, Dipropylene Glycol Dibenzoate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Aqua, Polyacrylate-42, Acetyl Tributyl Citrate, Dibutyl Sebacate, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Aqua, Polyacrylate-42, Dibutyl Sebacate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Methyl Soyate, Ethyl Lactate, Simmondsia Chinensis Seed Oil A nail polish base with very fast curing and high final hardness. After curing the nail polish has a good scratch resistance and gloss retention. It is less flexible than 200 and can also be used without base and top coat. A nail polish base with very fast curing and a little more flexibility than 100. After curing the nail polish has a good scratch resistance and gloss retention. It can also be used without base and top coat. A sticky nail polish base with good adhesion to the nail. The fast drying shortens the waiting time before applying additional coats. Extends the wearing time of the nail polish, since impacts are mitigated and the paint does not peel off from the nail. A very hard and high gloss top coat with a short curing time. Very scratch resistant and slippery to prevent loss of gloss. Vegetable based nail polish remover. For easy removal of aqueous nail polishes with moisturizing and nourishing properties. I 2 I
Typical Properties Properties 100 200 Base Coat Top Coat INCI Aqua, Polyacrylate-42, Dibutyl Sebacate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Aqua, Polyacrylate-42, Dipropylene Glycol Dibenzoate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Aqua, Polyacrylate-42, Acetyl Tributyl Citrate, Dibutyl Sebacate, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Aqua, Polyacrylate-42, Dibutyl Sebacate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Color White emulsion White emulsion White emulsion White emulsion Viscosity 4000 mpas 4000 mpas 4000 mpas 4000 mpas ph Value 8.0 9.0 8.0 9.0 8.0 9.0 8.0 9.0 Preservatives No* No* No* No* *Annex V of the EU Cosmetic Regulation EC No 1223/2009; Annex 3 of the Japanese Standards for Cosmetics I 3 I
Typical Properties Removing of nail polish Properties INCI Color Viscosity Natural Remover Methyl Soyate, Ethyl Lactate, Simmondsia Chinensis Seed Oil Clear, yellowish liquid 50 mpas The best time to remove water-based nail polish is directly after a bath or shower. The nail polish will have absorbed water and be easier to remove. Otherwise, you can soak your nails in warm water for five minutes. Put one drop of nail polish remover on each nail and allow the remover to soak for about one minute. Rub the nails with a well-soaked cotton pad until the polish is fully removed. If a small amount of polish is left on the sides of your nails, use a wood cuticle stick to gently scrape off the polish. Wash your hands with soap and water and dry them. I 4 I
Nail Polish Additives Rheology modifiers Thickeners Slip additives Silicones Wetting agents Fillers Antifoams Dispersants UV screens Therapeutic agents (actives) Moisturizers Film-Former Non-film-forming polymers Aqua Thix, Acrylates, Bentonite, Hectorite, Silica Aqua Thix, Acrylates, Bentonite, Hectorite, Silica Wax, Silicone Gums, Dimethiconol Dimethicone, PEG/PPG-Dimethicone, Siloxane Silicone, Surfactants Talc, Barium Sulfate Silicone WorléeMicromer C50/25, Ester, Acrylates Water soluble UV screens Spirulina, Bitrex, Plant extracts etc Glycerin, Sorbitol WorléeMicromers, Polyurethane, Acrylates Polyester, Acrylates Perfumes, preservatives, neutralizing agents, antioxidants I 5 I
Nail Polish Top Coat 100 & 200 Base Coat Nail Top Coat 100 & 200 Nail 100 & 200 Base Coat Nail 100 & 200 Nail I 6 I
Performance Drying Time Gloss Durability 1 2 3 4 5 6 Opacity Smell Application Water-Based Solvent-Based 1: Good 6: Worse For the test, the three different nail polishes were applied to the nails of female test subjects. After a drying time of one hour, dishwashing was simulated for five minutes. In the next step, the test persons had to grasp with both hands in stone chippings (10 times). The hands were photographed after the test (see below). The nail polishes were compared in the six categories. Water-Based Solvent-Based I 7 I
Performance Smell Application 1 1 2 2 3 3 4 4 5 6 Water-Based Solvent-Based 5 6 Water-Based Solvent-Based Upper Quartile Minimum Median Mean Maximum Lower Quartile Upper Quartile Minimum Median Mean Maximum Lower Quartile I 8 I
Performance Opacity Gloss 1 1 2 2 3 3 4 4 5 6 Water-Based Solvent-Based 5 6 Water-Based Solvent-Based Upper Quartile Minimum Median Mean Maximum Lower Quartile Upper Quartile Minimum Median Mean Maximum Lower Quartile I 9 I
Performance Drying Time Durability 1 1 2 2 3 3 4 4 5 6 Water-Based Solvent-Based 5 6 Water-Based Solvent-Based Upper Quartile Minimum Median Mean Maximum Lower Quartile Upper Quartile Minimum Median Mean Maximum Lower Quartile I 10 I
Gloss Retention [%] Performance Abrasion resistance with crock meter 50dr 9μ sandpaper 1st bar gloss 20-2nd bar gloss 60 100 80 60 40 20 0 I 11 I
Pendulum hardness König [s] Performance Film hardness evaluation - 100µm film 125 100 75 50 25 0 0 2 4 6 8 10 12 14 16 18 20 22 24 Drying time in hours 100 200 Top Coat Solvent-Based 1 Solvent-Based 2 Solvent-Based 3 Solvent-Based 4 Water-Based 1 Water-Based 2 I 12 I
Solubility 100µm film on glass plate WorléeMicromer C20/41 Start of water absorption Peeling / dissolving of the film WorléeMicromer C60/42 WorléeMicromer C70/61 >24h WorléeMicromer C70/63 >24h WorléeMicromer C80/50 <24h WorléeMicromer C50/25 100 / 200 >24h 15 min 30 min 60 min 120 min 180 min I 13 I
Benefits without preservatives excellent drying time very short curing time waterproof no hazardous material (except remover) residual monomer content 50ppm, thereof styrene 10ppm freeze/thaw stable shear tolerant temperature tolerant compatible with ethanol and glycols I 14 I
Formulations Water-based Nail Polish Pure Red Pure bright red nail polish with excellent opacity contains 100 with excellent curing for early and high scratch resistance. The formulation is prepared without expensive equipment in the cold process. With the help of the aqueous pigment pastes WorléeBase the color is adjusted in a simple and dust-free manner. Simple, lean and cost-effective. Phase Ingredient INCI Supplier % A 100 Aqua, Polyacrylate-42, Dibutyl Sebacate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Worlée 94.00 B WorléeBase AQ 15850:1/1 Aqua and CI 15850:1, Barium Sulfate, Ammonium Acrylates Copolymer, Methylpropanediol, Sodium Acrylates Copolymer, Caprylyl Glycol, Phenylpropanol, Simethicone Worlée 6.00 Total: 100.00 Procedure: Weigh in phase A and begin stirring. Add phase B and stir until uniform. I 15 I
Formulations Water-based Nail Polish Blue Denim Inspired by denim, this glossy and blue colored nail polish contains 200 to get more flexibility and high scratch resistance. The formulation is prepared without expensive equipment in the cold process. With the help of the aqueous pigment pastes WorléeBase the color is adjusted in a simple and dust-free manner. Simple, lean and cost-effective. Phase Ingredient INCI Supplier % A 200 Aqua, Polyacrylate-42, Dipropylene Glycol Dibenzoate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Worlée 90.70 B HDK H20 Silica Dimethyl Silylate Wacker 1.00 C WorléeBase AQ 77007/1 CI 77007, Aqua, Methylpropanediol, Ammonium Acrylates Copolymer, Sodium Acrylates Copolymer, Simethicone, Caprylyl Glycol, Phenylpropanol Worlée 7.10 WorléeBase AQ 77266/1 Aqua, Ammonium Acrylates Copolymer, CI 77266 (nano), Methylpropanediol, Simethicone, Caprylyl Glycol, Phenylpropanol Worlée 0.20 D Syncrystal Soft Silver Synthetic Fluorphlogopite, Titanium Dioxide, Tin Oxide Eckart 1.00 Total: 100.00 Procedure: Weigh in phase A and begin stirring. Add all other phases separately and stir until uniform. I 16 I
Formulations Water-based Nail Polish Just Black Deep, dark and cool look with a sophisticated style. This glossy and black colored nail polish contains 100 to get more flexibility and high scratch resistance. The formulation is prepared without expensive equipment in the cold process. With the help of the aqueous pigment pastes WorléeBase the color is adjusted in a simple and dust-free manner. Simple, lean and cost-effective. Phase Ingredient INCI Supplier % A 100 Aqua, Polyacrylate-42, Dibutyl Sebacate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Worlée 96.50 B WorléeBase AQ 77266/1 Aqua, Ammonium Acrylates Copolymer, CI 77266 (nano), Methylpropanediol, Simethicone, Caprylyl Glycol, Phenylpropanol Worlée 3.50 Total: 100.00 Procedure: Weigh in phase A and begin stirring. Add phase B and stir until uniform. I 17 I
Formulations Water-based Nail Polish Top Coat Scratch resistant top coat with very high gloss. Phase Ingredient INCI Supplier % A Top Coat Aqua, Polyacrylate-42, Dibutyl Sebacate, PPG-2 Methyl Ether, Oxidized Polyethylene, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Worlée 95.00 B Water Aqua 5.00 Total: 100.00 Procedure: Weigh in phase A and begin stirring. Add phase B to adjust viscosity and stir until uniform. Water-based Nail Polish Base Coat Quick-drying base coat with adjusted flexibility and good adhesion. Phase Ingredient INCI Supplier % A Base Coat Aqua, Polyacrylate-42, Acetyl Tributyl Citrate, Dibutyl Sebacate, Phenylpropanol, Caprylyl Glycol, Decylene Glycol Worlée 95.00 B Water Aqua 5.00 Total: 100.00 Procedure: Weigh in phase A and begin stirring. Add phase B to adjust viscosity and stir until uniform. I 18 I
Formulations Nail Polish Remover Vegetable based nail polish remover. For easy removal of aqueous nail polishes with moisturizing and nourishing properties. Phase Ingredient INCI Supplier % A B Natural Remover Fragrance Lemongrasstea P0240119 Methyl Soyate, Ethyl Lactate, Simmondsia Chinensis Seed Oil Worlée q.s. Parfum Frey + Lau q.s. Total: 100.00 Procedure: Weigh in phase A and begin stirring. Add phase B and stir until uniform. I 19 I